Home / UP Products / Wear Plates & Pipes

  • Wear Pipe

    • Welded pipe

      • Pipe diameter is relatively unrestricted
      • Pipe length is relatively unrestricted
      • Minimum internal radius of the pipe: 80 mm
      • Recommended hardfacing thickness: ≥ 4 mm
      • Recommended base metal thickness: ≥ 5 mm
      Welded pipe

    • Seamless pipe

      • Internal cladding technology for seamless steel pipes
      • Avoid weak zones associated with steel plate joints
      • Maintain good roundness
      • Minimum internal radius of the pipe: 76 mm
      • Maximum pipe length is 10 times the outer diameter length
      • Recommended hardfacing thickness: ≥ 4 mm
      • Recommended base metal thickness: ≥ 5 mm
      PDF Downloads
      Seamless pipe

  • Wear Plate

    Wear Plate Features

    • Fine and Uniform Chromium Carbide Precipitates
    • Superior Wear Resistance
    • Flat Wear Plate Surface
    • Consistent Hardness of the Hardfacing Layer
    • High Bonding Strength at the Hardfacing/Base Metal Interface
    • Excellent Workability / Excellent Machinability
    • Wear Plate Surface
      Wear Plate Surface
    • Chromium Carbide
      Chromium Carbide
    Standard Specifications (Excluding New Products)
    Length x Width Thickness (Base Layer + Hardfacing Layer)

    1200 x 2400

    3+3, 4+4, 6+4, 6+6, 8+5, 8+6, 10+10, 12+12, 12+20, 12+25

    1500 x 3000

    2200 x 3000

    • UP-X

      • * Undiluted hardness of the hardfacing
      • † Undiluted wear resistance data of the hardfacing
      PDF Downloads
      Hardness* (HRC) ASTM G65 Temperature resistance Features
      UP-X ≥58 ≤0.19 450 oC Suitable for sand and gravel abrasion

    • UP-N

      • * Undiluted hardness of the hardfacing
      • † Undiluted wear resistance data of the hardfacing
      PDF Downloads
      Hardness* (HRC) ASTM G65 Temperature resistance Features
      UP-N ≥60 ≤0.17 450 oC Suitable for severe sand and gravel abrasion

    • UP-H

      • * Undiluted hardness of the hardfacing
      • † Undiluted wear resistance data of the hardfacing
      PDF Downloads
      Hardness* (HRC) ASTM G65 Temperature resistance Features
      UP-H ≥60 ≤0.18 650 oC Suitable for high-temperature abrasion

    • UP-I

      • * Undiluted hardness of the hardfacing
      • † Undiluted wear resistance data of the hardfacing
      PDF Downloads
      Hardness* (HRC) ASTM G65 Temperature resistance Features
      UP-I ≥57 ≤0.20 450 oC Suitable for severe abrasion and impact

    • UP-F

      • * Undiluted hardness of the hardfacing
      • † Undiluted wear resistance data of the hardfacing
      PDF Downloads
      Hardness* (HRC) ASTM G65 Temperature resistance Features
      UP-F ≥61 ≤0.17 450 oC Ultra-thin wear plate

    • UP-T

      • * Undiluted hardness of the hardfacing
      • † Undiluted wear resistance data of the hardfacing
      PDF Downloads
      Hardness* (HRC) ASTM G65 Temperature resistance Features
      UP-T ≥2000 HV (Carbide) ≥500 HV (Matrix) ≤0.07 350 oC Suitable for extreme sand and gravel abrasion

    • UP-S

      • * Undiluted hardness of the hardfacing
      • † Undiluted wear resistance data of the hardfacing
      PDF Downloads
      Hardness* (HRC) ASTM G65 Temperature resistance Features
      UP-S ≤0.20 ≤0.07 450 oC Weld-free wear plate